PVC Granules of Various Grades and Specifications

• Customization: Available
• Carrier: PVC
• Color: White
• Model NO.: QS-800F, QS-850F, QS-1000F, QS-1050P, QS-1200
• Certification: ISO
• Transport Package: 25kgs Bag, 17mt/20FCL, 26.5mt/40FCL.
• Specification: 25kg/bags
• Trademark: Shandong Quanhua
• Origin: Shandong
• HS Code: 3904109090
• Production Capacity: 5000tons/Month

Product Description

Polyvinylchloride Resin (PVC)

   PVC is a kind of amorphous high polymer, whose glassing temperature is 105-75, while swells or dissolves in ether, ketone and aromatics. ºC to its molecular weight. Comparing with other common plastics, PVC has the characteristics of fire resistance and self-extinguishment, and extremely fine chemical corrosion resistance, electro-insulating property, chemical stability and thermo-plasticity. It's insoluble in water, alcohol. Visually PVC resin is white amorphous powder with particle size of 60-250um and apparent density 0.40-0.60g/ml. Under normal temperature, 100g resin can absorb 14-27g plasticizer.
 QILU brand PVC is produced with the patent technology of Japanese Shinetsu Chemical Company Ltd. and American Oxy Vinyls Company with introduced package equipments. 14 grades of products with different performances and uses can be made by applying the process of suspension polymerization and consuming VCM as its feedstock.  The main grades of QILU brand PVC are: S-700, S-800, S-1000, S-1300, QS-650, QS-800F, QS-850F, QS-1000F, QS-1050P, QS-1200 and QS-1350F. Mark, package, transportation and storage of PVC products:
 Mark      Trademark, product name, product grade, product standard number, net content, lot number, manufacturer name and address should be marked on the package of PVC.
 Package   PVC resin is packed with compound bag of kraft paper and PP woven material, or internally coated PP woven cloth exterior bag with LDPE film-lined interior bag, or in bulk. The seal of packing bag should guarantee the products not to be polluted or leaked during normal transportation and storage. The net content of small package is 25kg per bag, while big package is 1250kg, 1000kg, 600k or 500kg. 
Transportation Clean and covered transportation vehicle should be used for transportation of PVC to prevent from rain.
 Storage   PVC should be stored in dry and well-ventilated warehouses, which should be separated by lot to prevent from mixing lot numbers and can't be stacked in open air to prevent from solarizing and dampness.
       Grade S-700 is mainly used to produce transparent flakes, and can be pressed to hard or semi-hard slice or sheet for package, floor material, hard film for lining (for candy wrapping paper or cigarette packing film), etc. It can also be extruded to hard or semi-hard slice, sheet, or irregularly shaped bar for package. Or it can be injected to make joints, valves, electric parts, auto accessories and vessels.       

Grade			PVC S-700	Remarks
Item		Guarantee value	Test method
Average polymerization degree		650-750	GB/T 5761,Appendix A	K value 58-60
Apparent density, g/ml		0.52-0.62	Q/SH3055.77-2006, Appendix B
Volatiles content (water included), %,       ≤		0.30	Q/SH3055.77-2006, Appendix C
Plasticiser absorption of 100g resin, g,      ≥		14	Q/SH3055.77-2006, Appendix D
VCM residue, mg/kg                                     ≤		5	GB/T 4615-1987
Screenings %	0.25mm mesh              ≤	2.0	Method 1: GB/T 5761, Appendix B Method2: Q/SH3055.77-2006, Appendix A
	0.063mm mesh            ≥	95
Fisheye number, No./400cm^2,                   ≤		30	Q/SH3055.77-2006, Appendix E
Number of impurity particles, No.,             ≤		20	GB/T 9348-1988
Whiteness (160ºC, 10 minutes later), %,   ≥		75	GB/T 15595-95

        
       Grade S-800 is mainly used to produce transparent flakes, and can be pressed to hard or semi-hard slice or sheet for package, floor material, hard film for lining (for candy wrapping paper or cigarette packing film), etc. It can also be extruded to hard or semi-hard slice or sheet for package, sheet, or irregularly shaped bar. Or it can be injected to make joints, valves, electric parts, auto accessories and vessels.   
 

Grade			PVC S-800	Remarks
Item		Guarantee value	Test method
Average polymerization degree		750-850	GB/T 5761,Appendix A	K value 60-62
Apparent density, g/ml		0.51-0.61	Q/SH3055.77-2006, Appendix B
Volatiles content (water included), %,         ≤		0.30	Q/SH3055.77-2006, Appendix C
Plasticiser absorption of 100g resin, g,       ≥		16	Q/SH3055.77-2006, Appendix D
VCM residue, mg/kg                                       ≤		5	GB/T 4615-1987
Screenings %	2.0	2.0	Method 1: GB/T 5761, Appendix B Method 2: Q/SH3055.77-2006, Appendix A
	95	95
Fisheye number, No./400cm^2,                    ≤		30	Q/SH3055.77-2006, Appendix E
Number of impurity particles, No.,              ≤		20	GB/T 9348-1988
Whiteness (160ºC, 10 minutes later), %,    ≥		75	GB/T 15595-95

 
    Grade S-1000 can be used to produce soft film, sheet, manmade leather, piping, shaped bar, bellow, cable protection piping, packing film, sole and other soft sundry goods.  

Grade			PVC S-1000	Remarks
Item		Guarantee value	Test method
Average polymerization degree		970-1070	GB/T 5761,Appendix A	K value 65-67
Apparent density, g/ml		0.48-0.58	Q/SH3055.77-2006, Appendix B
Volatiles content (water included), %,    ≤		0.30	Q/SH3055.77-2006, Appendix C
Plasticiser absorption of 100g resin, g,   ≥		20	Q/SH3055.77-2006, Appendix D
VCM residue, mg/kg                               ≤		5	GB/T 4615-1987
Screenings %	2.0	2.0	Method 1: GB/T 5761, Appendix B Method 2: Q/SH3055.77-2006, Appendix A
	95	95
Fisheye number, No./400cm^2,                   ≤		20	Q/SH3055.77-2006, Appendix E
Number of impurity particles, No.,           ≤		16	GB/T 9348-1988
Whiteness (160ºC, 10minutes later), %,  ≥		78	GB/T 15595-95

 
     Grade S-1300 is mainly used to produce high-strength flexible products, pressed materials, rigid and flexible extrusion molding and insulating materials, etc. .

Grade			PVC S-1300	Remarks
Item		Guarantee value	Test method
Average polymerization degree		1250-1350	GB/T 5761,Appendix A	K value 71-73
Apparent density, g/ml		0.42-0.52	Q/SH3055.77-2006, Appendix B
Volatiles content (water included), %,           ≤		0.30	Q/SH3055.77-2006, Appendix C
Plasticiser absorption of 100g resin, g,          ≥		27	Q/SH3055.77-2006, Appendix D
VCM residue, mg/kg                                         ≤		5	GB/T 4615-1987
Screenings %	2.0	2.0	Method 1: GB/T 5761, Appendix B Method 2: Q/SH3055.77-2006, Appendix A
	95	95
Fisheye number, No./400cm^2,                        ≤		20	Q/SH3055.77-2006, Appendix E
Number of impurity particles, No.,                ≤		16	GB/T 9348-1988
Whiteness (160ºC, 10 minutes later), %,      ≥		78	GB/T 15595-95
Water extracts conductivity, S/cm·g,             ≤		5	GB 2915-1999

 
Grade QS-650 is used for injection molding, pipe fittings, pressed material, rigid foam section, floor material, and extrusion rigid section, etc.   

Grade			PVC QS-650	Remarks
Item		Guarantee value	Test method
Average polymerization degree		600-700	GB/T 5761,Appendix A	K value 57-59
Apparent density, g/ml		0.53-0.60	Q/SH3055.77-2006, Appendix B
Volatiles content (water included), %,     ≤		0.40	Q/SH3055.77-2006, Appendix C
Plasticiser absorption of 100g resin, g,   ≥		15	Q/SH3055.77-2006, Appendix D
VCM residue, mg/kg                                                ≤		5	GB/T 4615-1987
Screenings %	2.0	2.0	Method 1: GB/T 5761, Appendix B Method 2: Q/SH3055.77-2006, Appendix A
	95	95
Fisheye number, No./400cm^2,                        ≤		30	Q/SH3055.77-2006, Appendix E
Number of impurity particles, No.,                ≤		20	GB/T 9348-1988
Whiteness (160ºC, 10 minutes later), %,      ≥		78	GB/T 15595-95

 
Grade QS-800F is used for extrusion section, wire and cable material, flexible and rigid material, rigid or semi-rigid pressed material, and flexible film and sheet.
 

Grade			PVC QS-800F	Remarks
Item		Guarantee value	Test method
Average polymerization degree		750-850	GB/T 5761,Appendix A	K value 60-62
Apparent density, g/ml		0.51-0.61	Q/SH3055.77-2006, Appendix B
Volatiles content (water included), %,          ≤		0.30	Q/SH3055.77-2006, Appendix C
Plasticiser absorption of 100g resin, g,         ≥		17	Q/SH3055.77-2006, Appendix D
VCM residue, mg/kg                                        ≤		5	GB/T 4615-1987
Screenings %	2.0	2.0	Method 1: GB/T 5761, Appendix B Method2:Q/SH3055.77-2006, Appendix A
	95	95
Fisheye number, No./400cm^2,                        ≤		30	Q/SH3055.77-2006, Appendix E
Number of impurity particles, No.,                ≤		20	GB/T 9348-1988
Whiteness (160ºC, 10 minutes later), %,      ≥		78	GB/T 15595-95

Grade QS-850F is used to produce injection molding, pipe fittings, pressed material, rigid foam section, floor material and extrusion rigid section, etc.,
 

Grade			PVC QS-850F	Remarks
Item		Guarantee value	Test method
Average polymerization degree		800-900	GB/T 5761,Appendix A	K value 62-64
Apparent density, g/ml		0.52	Q/SH3055.77-2006, Appendix B
Volatiles content (water included), %,          ≤		0.30	Q/SH3055.77-2006, Appendix C
Plasticiser absorption of 100g resin, g,         ≥		20	Q/SH3055.77-2006, Appendix D
VCM residue, mg/kg                                        ≤		≥5	GB/T 4615-1987
Screenings %	2.0	2.0	Method 1: GB/T 5761, Appendix B Method 2: Q/SH3055.77-2006, Appendix A
	95	95
Fisheye number, No./400cm^2,                        ≤		20	Q/SH3055.77-2006, Appendix E
Number of impurity particles, No.,                ≤		16	GB/T 9348-1988
Whiteness (160ºC, 10 minutes later), %,      ≥		78	GB/T 15595-95

  
Grade QS-1000F is used to produce flexible film sheet, pressed material, piping molding-die
tools, wire and cable insulation material, etc..
 

Grade			PVC QS-1000F	Remarks
Item		Guarantee value	Test method
Average polymerization degree		950-1050	GB/T 5761,Appendix A	K value 65-67
Apparent density, g/ml		0.49	Q/SH3055.77-2006, Appendix B
Volatiles content (water included), %,     ≤		0.30	Q/SH3055.77-2006, Appendix C
Plasticiser absorption of 100g resin, g,    ≥		24	Q/SH3055.77-2006, Appendix D
VCM residue, mg/kg                                   ≤		≥5	GB/T 4615-1987
Screenings %	2.0	2.0	Method 1: GB/T 5761, Appendix B Method 2: Q/SH3055.77-2006, Appendix A
	95	95
Fisheye number, No./400cm^2,                  ≤		20	Q/SH3055.77-2006, Appendix E
Number of impurity particles, No.,          ≤		16	GB/T 9348-1988
Whiteness (160ºC, 10 minutes later), %,≥		80	GB/T 15595-95

  
Grade QS-1050P is used to produce irrigation pipe, potable water pipe, foam-core pipe, electric wire conduit, rigid shaped section, etc..   
 

Grade			PVC QS-1050P	Remarks
Item		Guarantee value	Test method
Average polymerization degree		1000-1100	GB/T 5761,Appendix A	K value 66-68
Apparent density, g/ml		0.51-0.57	Q/SH3055.77-2006, Appendix B
Volatiles content (water included), %,     ≤		0.30	Q/SH3055.77-2006, Appendix C
Plasticiser absorption of 100g resin, g,    ≥		21	Q/SH3055.77-2006, Appendix D
VCM residue, mg/kg                                   ≤		5	GB/T 4615-1987
Screenings %	2.0	2.0	Method 1: GB/T 5761, Appendix B Method2: Q/SH3055.77-2006, Appendix A
	95	95
Fisheye number, No./400cm^2,                  ≤		20	Q/SH3055.77-2006, Appendix E
Number of impurity particles, No.,          ≤		16	GB/T 9348-1988
Whiteness (160ºC, 10 minutes later), %,≥		80	GB/T 15595-95

 
  
Grade QS-1200 can be used to produce flexible film and sheet, rigid extrusion material, piping molding-die tool, pressed material, wire and cable insulating material, etc.
 

Grade			PVC QS-1200	Remarks
Item		Guarantee value	Test method
Average polymerization degree		1150-1250	GB/T 5761,Appendix A	K value 69-71
Apparent density, g/ml		0.47	Q/SH3055.77-2006, Appendix B
Volatiles content (water included), %,     ≤		0.30	Q/SH3055.77-2006, Appendix C
Plasticiser absorption of 100g resin, g,    ≥		25	Q/SH3055.77-2006, Appendix D
VCM residue, mg/kg                                   ≤		≥5	GB/T 4615-1987
Screenings %	2.0	2.0	Method 1: GB/T 5761, Appendix B Method 2: Q/SH3055.77-2006, Appendix A
	95	95
Fisheye number, No./400cm^2,                  ≤		20	Q/SH3055.77-2006, Appendix E
Number of impurity particles, No.,          ≤		16	GB/T 9348-1988
Whiteness (160ºC, 10 minutes later), %,≥		80	GB/T 15595-95

  
  
Grade QS-1350 can be used to produce high-strength flexible products, pressed material, rigid or flexible extrusion section, and insulating material, etc..
 

Grade			PVC QS-1350F	Remarks
Item		Guarantee value	Test method
Average polymerization degree		1300-1400	GB/T 5761,Appendix A	K value 72-74
Apparent density, g/ml		0.47	Q/SH3055.77-2006, Appendix B
Volatiles content (water included), %,     ≤		0.30	Q/SH3055.77-2006, Appendix C
Plasticiser absorption of 100g resin, g,    ≥		27	Q/SH3055.77-2006, Appendix D
VCM residue, mg/kg                                   ≤		5	GB/T 4615-1987
Screenings %	2.0	2.0	Method 1: GB/T 5761, Appendix B Method 2: Q/SH3055.77-2006, Appendix A
	95	95
Fisheye number, No./400cm^2,                  ≤		20	Q/SH3055.77-2006, Appendix E
Number of impurity particles, No.,          ≤		16	GB/T 9348-1988
Whiteness (160ºC, 10 minutes later), %,≥		80	GB/T 15595-95
Water extracts conductivity, S/cm·g,       ≤		5	GB 2915-1999